Low-Temperature Electron Transport in [110] and [100] Silicon Nanowires: A DFT - Monte Carlo study

Shiri, Nekovei, Verma
The effects of very low temperature on the electron transport in a [110] and [100] axially aligned unstrained silicon nanowires (SiNWs) are investigated. A combination of semi-empirical 10-orbital tight-binding method, density functional theory (DFT), and Ensemble Monte Carlo (EMC) methods are used. Both acoustic and optical phonons are included in the electron-phonon scattering rate calculations covering both intra-subband and inter-subband events. A comparison with room temperature (300 K) characteristics shows that for both nanowires, the average electron steady-state drift velocity increases at least 2 times at relatively moderate electric fields and lower temperatures. Furthermore, the average drift velocity in [110] nanowires is 50 percent more than that of [100] nanowires, explained by the difference in their conduction subband effective mass. Transient average electron velocity suggests that there is a pronounced streaming electron motion at low temperature which is attributed to the reduced electron-phonon scattering rates.
academic

Low-Temperature Electron Transport in 110 and 100 Silicon Nanowires: A DFT - Monte Carlo study

基本信息

  • 论文ID: 2409.07282
  • 标题: Low-Temperature Electron Transport in 110 and 100 Silicon Nanowires: A DFT - Monte Carlo study
  • 作者: Daryoush Shiri (Chalmers University of Technology), Reza Nekovei (Texas A&M University-Kingsville), Amit Verma (Texas A&M University-Kingsville)
  • 分类: cond-mat.mes-hall cond-mat.mtrl-sci physics.comp-ph quant-ph
  • 发表时间: 2024年9月11日 (arXiv预印本)
  • 论文链接: https://arxiv.org/abs/2409.07282

摘要

本研究调查了极低温度对110和100轴向排列无应变硅纳米线(SiNWs)中电子输运的影响。采用半经验10轨道紧束缚方法、密度泛函理论(DFT)和集合蒙特卡罗(EMC)方法的组合。在电子-声子散射率计算中包括了声学和光学声子，覆盖子带内和子带间事件。与室温(300K)特性的比较表明，对于两种纳米线，在相对适中的电场和较低温度下，平均电子稳态漂移速度至少增加2倍。此外，110纳米线的平均漂移速度比100纳米线高50%，这由它们导带子带有效质量的差异解释。瞬态平均电子速度表明，在低温下存在明显的流电子运动，这归因于电子-声子散射率的降低。

研究背景与动机

1. 研究问题

本研究要解决的核心问题是理解极低温条件下硅纳米线中电子输运特性的变化规律，特别是不同晶向(110和100)硅纳米线在低温环境下的电子传输行为差异。

2. 问题重要性

  • 量子计算应用: 硅纳米线在基于自旋的量子比特(qubits)中显示出增强相干性的潜力，相比于III-V族纳米线，避免了与原子核的超精细磁相互作用限制
  • 低温电子学: 为CMOS兼容的低温传感器、开关和深空电子器件提供低成本替代方案
  • 技术兼容性: 硅纳米线制造与主流硅技术兼容，具有尺寸减小带来的增强量子力学效应

3. 现有研究局限性

  • 对硅纳米线在极低温下的电子输运机制理解不够深入
  • 缺乏不同晶向纳米线在低温下输运特性的系统比较
  • 对电子-声子散射在低温下的详细影响机制研究不足

4. 研究动机

随着量子计算和低温电子学的发展，需要深入理解硅纳米线在极低温下的电子输运特性，为相关器件设计提供理论基础。

核心贡献

  1. 多物理场耦合计算方法: 首次结合DFT、紧束缚方法和集合蒙特卡罗方法，系统研究硅纳米线低温电子输运
  2. 晶向依赖性揭示: 定量分析了110和100晶向硅纳米线在低温下的输运差异，发现110纳米线具有50%更高的漂移速度
  3. 散射机制阐明: 详细分析了声学和光学声子散射对低温电子输运的影响，包括子带内和子带间散射过程
  4. 流电子运动发现: 首次在硅纳米线中观察到低温下的流电子运动现象，并提供了物理机制解释
  5. 低温输运增强量化: 证明低温下电子漂移速度至少提高2倍，为低温器件设计提供定量指导

方法详解

任务定义

研究在4K和300K温度下，110和100晶向硅纳米线在不同电场作用下的电子输运特性，包括稳态和瞬态漂移速度。

模型架构

1. 结构优化与能带计算

  • DFT计算: 使用SIESTA代码进行结构能量最小化
    • 交换相关泛函: 广义梯度近似(GGA)与PBE赝势
    • k点采样: 1×1×40 (Monkhorst-Pack算法)
    • 能量截止: 680 eV
    • 力容差: 0.01 eV/Å
  • 紧束缚方法: 采用半经验sp³d⁵s*紧束缚方案
    • 10轨道模型
    • 参数来自Jancu等人(1998)
    • 布里渊区划分为8000个网格点

2. 电子-声子散射率计算

散射率基于一阶微扰理论和形变势近似计算:

声学声子: 采用德拜近似

  • 线性色散关系: EP=ℏω=c∣k∣E_P = \hbar\omega = c|k|
  • 其中c为硅中声速

光学声子: 平坦色散

  • 能量固定: ELO=54E_{LO} = 54 meV

散射率温度依赖性:

  • 声子发射: 正比于 n(EP)+1n(E_P) + 1
  • 声子吸收: 正比于 n(EP)n(E_P)
  • 声子占据数: n(EP)=1eEP/kBT−1n(E_P) = \frac{1}{e^{E_P/k_BT} - 1}

3. 集合蒙特卡罗模拟

  • 包含4个最低导带子带
  • 考虑子带内和子带间散射
  • 稳态分析: t=0时刻在最低导带底注入电子
  • 瞬态分析: 先在零电场下运行50,000次迭代达到平衡

技术创新点

  1. 多尺度建模: 将原子尺度的DFT计算与介观尺度的输运模拟相结合
  2. 全面散射考虑: 同时包含声学和光学声子的子带内外散射
  3. 温度效应精确处理: 通过Bose-Einstein分布精确计算温度对散射的影响
  4. 瞬态动力学分析: 揭示电子在动量空间的"弹跳"行为

实验设置

纳米线结构参数

  • 110 SiNW: 直径1.3 nm，氢钝化表面
  • 100 SiNW: 直径1.1 nm，氢钝化表面
  • 边界条件: 自由站立，相邻单胞最小距离>0.6 nm

计算参数

  • 温度: 4K (低温) 和 300K (室温)
  • 电场范围: 0-50 kV/cm
  • 能带参数:
    • 110: Ecmin=1.81E_{cmin} = 1.81 eV, m∗=0.16m^* = 0.16
    • 100: Ecmin=2.528E_{cmin} = 2.528 eV, m∗=0.63m^* = 0.63

评价指标

  • 平均漂移速度 vs 电场
  • 瞬态速度演化
  • 电子分布函数时间演化
  • 散射率与温度和晶向的关系

实验结果

主要结果

1. 稳态漂移速度

  • 低温增强: 4K下漂移速度比300K提高至少2倍
  • 晶向差异: 110纳米线漂移速度比100高约50%
  • 速度饱和: 高电场下由于声子发射散射导致速度饱和

2. 散射率分析

  • 温度依赖: 低温下散射率显著降低，主要由声子发射主导
  • 晶向效应: 100纳米线散射率比110高约2倍
  • van Hove奇点: LO声子散射率在能带底部出现尖峰

3. 瞬态行为

  • 流电子运动: 低温下观察到明显的速度振荡
  • 弹跳机制: 电子在动量空间的周期性加速-散射过程
  • 时间尺度: 振荡周期约600 fs

关键数据

  • 15 kV/cm电场下，100纳米线速度降低约1/5，110降低约1/2 (4K→300K)
  • 有效质量比: 100/110 = 0.63/0.16 ≈ 4
  • LO声子散射阈值: k ≈ 2×10⁶ cm⁻¹ (110), k ≈ 6×10⁶ cm⁻¹ (100)

物理机制解释

  1. 低温增强: n(EP)→0n(E_P) → 0时声子吸收散射消失，主要为发射过程
  2. 晶向差异: 有效质量差异导致态密度不同，DOS(E)∝m∗DOS(E) ∝ \sqrt{m^*}
  3. 流运动: 电子达到LO声子发射阈值后快速散射回k=0附近，形成周期性运动

相关工作

主要研究方向

  1. 硅纳米线制造: 自上而下和自下而上制造方法
  2. 量子器件应用: 自旋量子比特、量子点器件
  3. 低温电子学: 深空电子器件、低温传感器
  4. 输运理论: 纳米尺度电子输运建模

本文优势

  • 首次系统研究硅纳米线低温输运的晶向依赖性
  • 结合第一性原理与输运模拟的多尺度方法
  • 发现并解释了流电子运动现象

结论与讨论

主要结论

  1. 低温显著增强硅纳米线电子输运性能
  2. 110晶向纳米线具有更优的输运特性
  3. 电子-声子散射的温度依赖性是关键物理机制
  4. 低温下存在独特的流电子运动现象

局限性

  1. 理想化假设: 假设纳米线无缺陷、无掺杂、均匀温度
  2. 尺寸限制: 仅研究了特定直径的纳米线
  3. 散射机制: 未考虑界面散射、杂质散射等其他机制
  4. 实验验证: 缺乏相应的实验验证数据

未来方向

  1. 考虑表面粗糙度和缺陷的影响
  2. 扩展到更多晶向和尺寸
  3. 研究应变对低温输运的影响
  4. 开发相应的实验验证方法

深度评价

优点

  1. 方法创新: 多物理场耦合计算方法具有很强的创新性
  2. 物理洞察: 对流电子运动现象的发现和解释具有重要物理意义
  3. 实用价值: 为低温硅基器件设计提供重要指导
  4. 计算严谨: DFT+TB+EMC的组合方法计算严谨可靠

不足

  1. 实验缺失: 缺乏实验验证，理论预测需要实验支持
  2. 参数敏感性: 未充分讨论计算参数对结果的敏感性
  3. 应用局限: 研究的纳米线尺寸和条件相对有限
  4. 机制分析: 对某些物理现象的微观机制解释还可以更深入

影响力

  1. 学术贡献: 为纳米尺度低温电子输运理论提供重要补充
  2. 技术指导: 对硅基量子器件和低温电子学发展具有指导意义
  3. 方法示范: 多尺度计算方法可推广到其他纳米材料研究

适用场景

  1. 硅基量子计算器件设计
  2. 低温电子学器件开发
  3. 深空探测电子系统
  4. 高性能纳米电子器件

参考文献

本文引用了67篇相关文献，涵盖了硅纳米线制造、量子器件、低温电子学和输运理论等多个领域的重要工作，为研究提供了坚实的理论基础。

总体评价: 这是一篇高质量的理论计算论文，采用多尺度建模方法系统研究了硅纳米线低温电子输运特性，发现了重要的物理现象并提供了合理的机制解释。研究结果对硅基量子器件和低温电子学具有重要指导意义，但需要进一步的实验验证来支持理论预测。