Wear and corrosion properties of Mg(OH)$_2$ compound layer formed on magnesium alloy in superheated water vapor

Peng, Wang
The wear resistance of magnesium and its alloys is very poor due to their inherent low hardness and poor tribological properties. Improving the wear resistance of magnesium and its alloys plays a significant role in expanding their application range. Various surface treatments have been used to produce protective coatings or layers for solving this problem. In this work, the Mg(OH)$_2$ layer with a thickness about 25 microns was directly formed on AZ91 magnesium alloy by oxidizing in superheated water vapor. SEM and XRD were employed to characterize the microstructure and phase composition of oxidized layer. The effect of oxidized layer on the friction and wear properties of magnesium alloy against the bearing steel ball were evaluated by using a reciprocating friction and wear test apparatus. The results showed that layer exhibited low friction coefficients and extremely small wear loss compared to the untreated substrate. Keywords: Magnesium alloy; Mg(OH)$_2$ layer; superheated water vapor; wear resistance.
academic

Wear and corrosion properties of Mg(OH)2_2 compound layer formed on magnesium alloy in superheated water vapor

基本信息

  • 论文ID: 2412.20959
  • 标题: Wear and corrosion properties of Mg(OH)2_2 compound layer formed on magnesium alloy in superheated water vapor
  • 作者: Tianxiang Peng, Liang Wang (Dalian Maritime University)
  • 分类: cond-mat.mtrl-sci (材料科学)
  • 通讯作者: Liang Wang (wlimt@dlmu.edu.cn)
  • 论文链接: https://arxiv.org/abs/2412.20959

摘要

镁及其合金由于固有的低硬度和较差的摩擦学性能导致其耐磨性很差。改善镁合金的耐磨性对扩大其应用范围具有重要意义。本研究通过在过热水蒸气中氧化,在AZ91镁合金表面直接形成了厚度约25微米的Mg(OH)2_2层。采用SEM和XRD表征了氧化层的微观结构和相组成。使用往复式摩擦磨损试验装置评估了氧化层对镁合金与轴承钢球摩擦磨损性能的影响。结果表明,与未处理基材相比,该层表现出较低的摩擦系数和极小的磨损损失。

研究背景与动机

问题描述

  1. 核心问题: 镁合金固有的低硬度和差的摩擦学性能导致其耐磨性极差,限制了其在滑动磨损部件中的应用
  2. 应用需求: 镁合金作为最轻的结构材料之一,具有优异的强度重量比,在航空航天和汽车工业中具有重要价值
  3. 腐蚀问题: 镁合金在腐蚀性介质甚至潮湿环境中的耐腐蚀性很差

研究重要性

  • 镁合金的轻质特性使其在燃油效率和性能要求严格的行业中具有关键优势
  • 改善耐磨性和耐腐蚀性是扩大镁合金应用范围的关键技术瓶颈
  • 表面处理技术是解决这一问题的有效途径

现有方法局限性

现有表面处理方法包括阳极氧化、化学转化、等离子电解氧化、电镀、摩擦搅拌处理、包覆、物理气相沉积等,但这些方法通常:

  • 工艺复杂,成本较高
  • 需要特殊设备和化学试剂
  • 可能产生环境污染
  • 涂层与基体结合力可能不足

研究动机

本文提出一种简单、环保的过热水蒸气氧化方法,仅需电能和少量水,无其他消耗品和排放物,通过镁的直接氧化形成Mg(OH)2_2保护层。

核心贡献

  1. 提出了环保简便的表面处理新方法: 开发了过热水蒸气氧化技术,在200°C下4小时处理即可形成25μm厚的Mg(OH)2_2
  2. 显著改善了摩擦学性能: 摩擦系数从0.4-0.5降至0.12-0.17,磨损率降低16-25倍
  3. 大幅提升了耐腐蚀性能: 在3.5% NaCl溶液中浸泡300小时后表面基本无变化
  4. 提供了系统的性能评价: 通过多种载荷条件下的摩擦磨损试验和长期腐蚀试验全面评估了处理效果
  5. 揭示了磨损机理变化: 从氧化-犁削-塑性变形-粘着的复合磨损转变为研磨-抛光机理

方法详解

材料与试样制备

  • 材料: AZ91D镁合金,化学成分(wt.%):Al(8.3-9.7),Zn(0.35-1.0),Mn(0.15-0.5),Mg(余量)
  • 试样: 从直径12mm棒材切取厚度5mm的试样
  • 预处理: 使用400-1200目碳化硅砂纸机械研磨

氧化处理工艺

  1. 设备: 不锈钢容器,总容积4.4升
  2. 工艺参数:
    • 温度:200°C
    • 保温时间:4小时
    • 介质:过热水蒸气
  3. 反应机理: Mg + 2H₂O → Mg(OH)₂ + H₂
  4. 特点:
    • 无需额外预处理
    • 仅消耗电能和少量水
    • 无其他消耗品和排放物

表征方法

  1. XRD分析: Rigaku D/Max-Ultima,Cu Kα辐射(λ=1.54 Å),40kV/40mA
  2. SEM观察: SUPRA 55扫描电镜,配备EDX分析系统
  3. 厚度测量: 通过抛光截面的显微镜观察

性能测试

  1. 摩擦磨损试验:
    • 设备:HRS-2M摩擦磨损试验机(销-盘配置)
    • 对偶件:GCr15轴承钢球(直径5mm)
    • 载荷:3N、5N、8N
    • 往复长度:5mm,频率:5Hz,时间:30分钟
    • 环境:室温,相对湿度40%,干滑动条件
  2. 腐蚀试验: 3.5% NaCl溶液浸泡试验,观察不同时间的腐蚀形貌

实验设置

试验材料

  • 基体材料: AZ91D镁合金
  • 对比样品: 未处理试样 vs 氧化处理试样
  • 对偶材料: GCr15轴承钢球

评价指标

  1. 摩擦学指标:
    • 摩擦系数(连续监测)
    • 磨损率(mm³N⁻¹m⁻¹)
    • 磨痕宽度和深度
  2. 腐蚀性能: 浸泡试验中的表面形貌变化
  3. 微观结构: 相组成、表面形貌、截面结构

测试条件

  • 载荷范围: 3N、5N、10N
  • 测试时间: 30分钟
  • 环境条件: 室温、干摩擦
  • 腐蚀介质: 3.5 wt.% NaCl溶液

实验结果

微观结构表征

  1. 外观变化: 处理后表面呈均匀深黑色
  2. 相组成: XRD确认形成Mg(OH)₂相,特征峰位于32.8°、38.1°、58.7°、62.2°和68.9°
  3. 层厚度: 约25μm,致密均匀无明显缺陷
  4. 元素组成: EDX显示O/Mg原子比接近2:1,证实为Mg(OH)₂

摩擦磨损性能

未处理试样结果

  • 摩擦系数: 0.35-0.45(3N、5N载荷),0.3-0.55(10N载荷)
  • 磨痕宽度: 930-1000μm(3N),1320-1400μm(5N),1520-1600μm(10N)
  • 磨痕深度: 45μm(3N),102μm(5N),127μm(10N)
  • 磨损率: 63.95×10⁻⁷(3N),84.14×10⁻⁷(5N),79.66×10⁻⁷ mm³N⁻¹m⁻¹(10N)

氧化处理试样结果

  • 摩擦系数: 0.12-0.17(所有载荷条件下)
  • 磨痕宽度: 535μm(3N),562μm(5N),622μm(10N)
  • 磨痕深度: 5μm(3N),7μm(5N),12μm(10N)
  • 磨损率: 3.96×10⁻⁷(3N),3.62×10⁻⁷(5N),3.12×10⁻⁷ mm³N⁻¹m⁻¹(10N)

性能改善幅度

  • 摩擦系数降低: 约70-75%
  • 磨损率降低: 16倍(3N),23倍(5N),25倍(10N)
  • 磨痕表面: 光滑平整,无明显划痕,呈抛光状

腐蚀性能

  • 未处理试样: 12小时出现局部腐蚀,48小时大面积腐蚀产物,72小时严重腐蚀,300小时部分完全腐蚀
  • 氧化处理试样: 300小时浸泡后表面基本无变化,无腐蚀产物

磨损机理分析

  1. 未处理试样:
    • 低载荷:氧化磨损和犁削
    • 高载荷:犁削、塑性变形和粘着的复合机理
  2. 氧化处理试样: 研磨和抛光机理,无划痕、粘着或塑性变形

相关工作对比

其他表面处理方法性能对比

  1. Ti-DLC涂层: 摩擦系数<0.12,磨损率降低2-3个数量级
  2. TiC/Co/Y₂O₃复合涂层: 磨损率降低约7倍
  3. Ti-MoS₂自润滑涂层: 磨损体积降低43.88%-89.78%
  4. Ni-WC/Al-Ni功能梯度涂层: 耐磨性提高5-8倍
  5. Nb₂O₅/Mg梯度涂层: 磨损率降低一个数量级以上

本方法优势

  • 工艺简单: 无需复杂设备和化学试剂
  • 环境友好: 仅需水和电能,无污染物排放
  • 结合力强: 通过镁的直接氧化形成,结合力优异
  • 性能优异: 磨损率降低16-25倍,效果显著

结论与讨论

主要结论

  1. 成功制备: 在200°C过热水蒸气中4小时成功制备25μm厚的Mg(OH)₂层
  2. 摩擦学性能显著改善: 摩擦系数从0.4-0.5降至0.12-0.17,磨损率降低16-25倍
  3. 耐腐蚀性大幅提升: 在3.5% NaCl溶液中300小时浸泡无明显腐蚀
  4. 磨损机理改变: 从复合磨损转变为温和的研磨抛光机理

技术创新点

  1. 工艺创新: 首次采用过热水蒸气直接氧化制备Mg(OH)₂保护层
  2. 环保特性: 绿色工艺,无化学污染
  3. 性能优异: 同时改善耐磨性和耐腐蚀性
  4. 机理清晰: 通过直接氧化确保优异的界面结合

局限性

  1. 处理温度: 需要200°C高温处理4小时
  2. 层厚限制: 目前层厚度约25μm,对于极端工况可能不足
  3. 载荷范围: 试验载荷相对较低(最高10N)
  4. 长期稳定性: 缺乏长期服役条件下的性能评价

未来方向

  1. 工艺优化: 研究温度、时间等参数对层厚度和性能的影响
  2. 性能提升: 探索复合处理技术进一步改善性能
  3. 应用拓展: 在实际工程条件下验证处理效果
  4. 机理深化: 深入研究Mg(OH)₂层的摩擦学机理

深度评价

优点

  1. 方法创新性强: 过热水蒸气氧化方法简单新颖,具有原创性
  2. 实验设计合理: 系统的表征和性能测试,数据可靠
  3. 结果显著: 摩擦磨损性能改善幅度大,实用价值高
  4. 环保意义: 绿色工艺符合可持续发展要求
  5. 机理分析到位: 通过多种手段揭示了性能改善机理

不足

  1. 载荷范围有限: 最高载荷仅10N,对重载工况适用性待验证
  2. 长期性能缺失: 缺乏长期服役性能和稳定性评价
  3. 成本分析不足: 未提供详细的经济性分析
  4. 应用场景有限: 主要针对干摩擦条件,湿润环境性能未知

影响力评估

  1. 学术贡献: 为镁合金表面处理提供了新思路和方法
  2. 实用价值: 工艺简单,易于工业化应用
  3. 环保意义: 符合绿色制造发展趋势
  4. 技术推广: 有望在镁合金表面处理领域得到应用

适用场景

  1. 轻载摩擦副: 适用于载荷相对较低的滑动部件
  2. 腐蚀环境: 海洋、化工等腐蚀性环境中的镁合金部件
  3. 航空航天: 对重量敏感的摩擦部件
  4. 汽车工业: 发动机、传动系统等轻量化部件

参考文献

论文引用了22篇相关文献,涵盖了镁合金表面处理的主要技术路线,包括阳极氧化、等离子电解氧化、物理气相沉积、化学气相沉积等方法,为本研究提供了充分的技术背景和对比基础。


总体评价: 这是一篇质量较高的材料科学研究论文,提出了一种简单环保的镁合金表面处理新方法,实验设计合理,结果令人信服。该方法在改善镁合金摩擦学性能方面效果显著,具有良好的应用前景。建议进一步开展长期性能评价和工程应用验证研究。