Wear and corrosion properties of Mg(OH)$_2$ compound layer formed on magnesium alloy in superheated water vapor

Peng, Wang
The wear resistance of magnesium and its alloys is very poor due to their inherent low hardness and poor tribological properties. Improving the wear resistance of magnesium and its alloys plays a significant role in expanding their application range. Various surface treatments have been used to produce protective coatings or layers for solving this problem. In this work, the Mg(OH)$_2$ layer with a thickness about 25 microns was directly formed on AZ91 magnesium alloy by oxidizing in superheated water vapor. SEM and XRD were employed to characterize the microstructure and phase composition of oxidized layer. The effect of oxidized layer on the friction and wear properties of magnesium alloy against the bearing steel ball were evaluated by using a reciprocating friction and wear test apparatus. The results showed that layer exhibited low friction coefficients and extremely small wear loss compared to the untreated substrate. Keywords: Magnesium alloy; Mg(OH)$_2$ layer; superheated water vapor; wear resistance.
academic

Propriétés d'usure et de corrosion de la couche composite Mg(OH)2_2 formée sur alliage de magnésium en vapeur d'eau surchauffée

Informations de base

  • ID de l'article: 2412.20959
  • Titre: Wear and corrosion properties of Mg(OH)2_2 compound layer formed on magnesium alloy in superheated water vapor
  • Auteurs: Tianxiang Peng, Liang Wang (Université maritime de Dalian)
  • Classification: cond-mat.mtrl-sci (Science des matériaux)
  • Auteur de correspondance: Liang Wang (wlimt@dlmu.edu.cn)
  • Lien de l'article: https://arxiv.org/abs/2412.20959

Résumé

Le magnésium et ses alliages présentent une très mauvaise résistance à l'usure en raison de leur faible dureté inhérente et de leurs mauvaises propriétés tribologiques. L'amélioration de la résistance à l'usure des alliages de magnésium est d'une importance capitale pour élargir leur gamme d'applications. Cette étude a formé directement une couche de Mg(OH)2_2 d'environ 25 micromètres d'épaisseur à la surface de l'alliage de magnésium AZ91 par oxydation en vapeur d'eau surchauffée. La microstructure et la composition de phase de la couche oxydée ont été caractérisées par MEB et DRX. L'effet de la couche oxydée sur les propriétés de frottement et d'usure entre l'alliage de magnésium et une bille d'acier à roulement a été évalué à l'aide d'un dispositif d'essai de frottement et d'usure alternatif. Les résultats montrent que cette couche présente un coefficient de frottement plus faible et une perte d'usure extrêmement faible par rapport au substrat non traité.

Contexte et motivation de la recherche

Description du problème

  1. Problème central: La faible dureté inhérente et les mauvaises propriétés tribologiques des alliages de magnésium entraînent une très mauvaise résistance à l'usure, limitant leur application dans les composants soumis à l'usure par glissement
  2. Besoins applicatifs: En tant que l'un des matériaux structuraux les plus légers, les alliages de magnésium possèdent un excellent rapport résistance-poids et présentent une valeur importante dans les industries aérospatiale et automobile
  3. Problème de corrosion: Les alliages de magnésium présentent une très mauvaise résistance à la corrosion dans les milieux corrosifs et même en environnement humide

Importance de la recherche

  • Les propriétés légères des alliages de magnésium leur confèrent un avantage clé dans les industries exigeant une efficacité énergétique et des performances strictes
  • L'amélioration de la résistance à l'usure et à la corrosion est un goulot d'étranglement technologique clé pour élargir la gamme d'applications des alliages de magnésium
  • Le traitement de surface est une voie efficace pour résoudre ce problème

Limitations des méthodes existantes

Les méthodes de traitement de surface existantes incluent l'anodisation, la conversion chimique, l'oxydation par décharge plasma électrolytique, l'électrodéposition, le traitement par friction-malaxage, le revêtement, la déposition physique en phase vapeur, etc., mais ces méthodes présentent généralement:

  • Des procédés complexes et des coûts élevés
  • La nécessité d'équipements spécialisés et de réactifs chimiques
  • Une pollution environnementale potentielle
  • Une adhérence insuffisante du revêtement au substrat

Motivation de la recherche

Cet article propose une méthode d'oxydation en vapeur d'eau surchauffée simple et respectueuse de l'environnement, nécessitant uniquement de l'énergie électrique et une petite quantité d'eau, sans autres consommables ni émissions, formant une couche protectrice de Mg(OH)2_2 par oxydation directe du magnésium.

Contributions principales

  1. Proposition d'une nouvelle méthode de traitement de surface écologique et simple: Développement d'une technologie d'oxydation en vapeur d'eau surchauffée, formant une couche de Mg(OH)2_2 de 25 μm d'épaisseur après un traitement de 4 heures à 200°C
  2. Amélioration significative des propriétés tribologiques: Le coefficient de frottement diminue de 0,4-0,5 à 0,12-0,17, le taux d'usure diminue de 16 à 25 fois
  3. Amélioration considérable de la résistance à la corrosion: Après immersion pendant 300 heures dans une solution NaCl à 3,5%, la surface reste pratiquement inchangée
  4. Fourniture d'une évaluation systématique des performances: Évaluation complète de l'effet du traitement par des essais de frottement et d'usure sous diverses conditions de charge et des essais de corrosion à long terme
  5. Révélation du changement du mécanisme d'usure: Transition d'un mécanisme d'usure composite (oxydation-labourage-déformation plastique-adhésion) à un mécanisme de polissage-rectification

Détails de la méthode

Matériaux et préparation des échantillons

  • Matériau: Alliage de magnésium AZ91D, composition chimique (% en poids): Al(8,3-9,7), Zn(0,35-1,0), Mn(0,15-0,5), Mg(reste)
  • Échantillons: Prélevés à partir d'une barre de diamètre 12 mm, épaisseur 5 mm
  • Prétraitement: Polissage mécanique à l'aide de papier abrasif au carbure de silicium 400-1200

Procédé de traitement par oxydation

  1. Équipement: Récipient en acier inoxydable, volume total 4,4 litres
  2. Paramètres du procédé:
    • Température: 200°C
    • Temps de maintien: 4 heures
    • Milieu: Vapeur d'eau surchauffée
  3. Mécanisme de réaction: Mg + 2H₂O → Mg(OH)₂ + H₂
  4. Caractéristiques:
    • Aucun prétraitement supplémentaire requis
    • Consommation uniquement d'énergie électrique et d'une petite quantité d'eau
    • Aucun autre consommable ni émission

Méthodes de caractérisation

  1. Analyse DRX: Rigaku D/Max-Ultima, rayonnement Cu Kα (λ=1,54 Å), 40kV/40mA
  2. Observation MEB: Microscope électronique à balayage SUPRA 55, équipé d'un système d'analyse EDX
  3. Mesure d'épaisseur: Observation microscopique de la section polie

Tests de performance

  1. Essai de frottement et d'usure:
    • Équipement: Machine d'essai de frottement et d'usure HRS-2M (configuration goupille-disque)
    • Matériau antagoniste: Bille d'acier à roulement GCr15 (diamètre 5 mm)
    • Charges: 3N, 5N, 8N
    • Longueur de course alternative: 5 mm, fréquence: 5 Hz, durée: 30 minutes
    • Environnement: Température ambiante, humidité relative 40%, conditions de frottement sec
  2. Essai de corrosion: Essai d'immersion dans une solution NaCl à 3,5%, observation de la morphologie de corrosion à différents moments

Configuration expérimentale

Matériaux d'essai

  • Matériau de base: Alliage de magnésium AZ91D
  • Échantillons de comparaison: Échantillons non traités vs. échantillons traités par oxydation
  • Matériau antagoniste: Bille d'acier à roulement GCr15

Indicateurs d'évaluation

  1. Indicateurs tribologiques:
    • Coefficient de frottement (surveillance continue)
    • Taux d'usure (mm³N⁻¹m⁻¹)
    • Largeur et profondeur des traces d'usure
  2. Performance de corrosion: Changements de morphologie de surface lors de l'essai d'immersion
  3. Microstructure: Composition de phase, morphologie de surface, structure en coupe transversale

Conditions d'essai

  • Plage de charges: 3N, 5N, 10N
  • Durée d'essai: 30 minutes
  • Conditions environnementales: Température ambiante, frottement sec
  • Milieu corrosif: Solution NaCl à 3,5% en poids

Résultats expérimentaux

Caractérisation de la microstructure

  1. Changement d'apparence: La surface traitée présente une couleur noire uniforme et profonde
  2. Composition de phase: La DRX confirme la formation de la phase Mg(OH)₂, avec des pics caractéristiques à 32,8°, 38,1°, 58,7°, 62,2° et 68,9°
  3. Épaisseur de la couche: Environ 25 μm, dense et uniforme sans défauts évidents
  4. Composition élémentaire: L'EDX montre un rapport atomique O/Mg proche de 2:1, confirmant la formation de Mg(OH)₂

Performance de frottement et d'usure

Résultats des échantillons non traités

  • Coefficient de frottement: 0,35-0,45 (charges 3N, 5N), 0,3-0,55 (charge 10N)
  • Largeur des traces d'usure: 930-1000 μm (3N), 1320-1400 μm (5N), 1520-1600 μm (10N)
  • Profondeur des traces d'usure: 45 μm (3N), 102 μm (5N), 127 μm (10N)
  • Taux d'usure: 63,95×10⁻⁷ (3N), 84,14×10⁻⁷ (5N), 79,66×10⁻⁷ mm³N⁻¹m⁻¹ (10N)

Résultats des échantillons traités par oxydation

  • Coefficient de frottement: 0,12-0,17 (toutes les conditions de charge)
  • Largeur des traces d'usure: 535 μm (3N), 562 μm (5N), 622 μm (10N)
  • Profondeur des traces d'usure: 5 μm (3N), 7 μm (5N), 12 μm (10N)
  • Taux d'usure: 3,96×10⁻⁷ (3N), 3,62×10⁻⁷ (5N), 3,12×10⁻⁷ mm³N⁻¹m⁻¹ (10N)

Ampleur de l'amélioration des performances

  • Réduction du coefficient de frottement: Environ 70-75%
  • Réduction du taux d'usure: 16 fois (3N), 23 fois (5N), 25 fois (10N)
  • Surface des traces d'usure: Lisse et plane, sans rayures évidentes, aspect poli

Performance de corrosion

  • Échantillons non traités: Corrosion locale après 12 heures, produits de corrosion généralisés après 48 heures, corrosion grave après 72 heures, corrosion partielle complète après 300 heures
  • Échantillons traités par oxydation: Surface pratiquement inchangée après 300 heures d'immersion, aucun produit de corrosion

Analyse du mécanisme d'usure

  1. Échantillons non traités:
    • Charges faibles: Usure par oxydation et labourage
    • Charges élevées: Mécanisme composite de labourage, déformation plastique et adhésion
  2. Échantillons traités par oxydation: Mécanisme de rectification et de polissage, sans rayures, adhésion ou déformation plastique

Comparaison avec les travaux connexes

Comparaison des performances avec d'autres méthodes de traitement de surface

  1. Revêtement Ti-DLC: Coefficient de frottement <0,12, taux d'usure réduit de 2-3 ordres de grandeur
  2. Revêtement composite TiC/Co/Y₂O₃: Taux d'usure réduit d'environ 7 fois
  3. Revêtement auto-lubrifiant Ti-MoS₂: Volume d'usure réduit de 43,88%-89,78%
  4. Revêtement à gradient fonctionnel Ni-WC/Al-Ni: Résistance à l'usure améliorée de 5-8 fois
  5. Revêtement à gradient Nb₂O₅/Mg: Taux d'usure réduit de plus d'un ordre de grandeur

Avantages de cette méthode

  • Procédé simple: Aucun équipement complexe ni réactif chimique requis
  • Respectueux de l'environnement: Nécessite uniquement de l'eau et de l'énergie électrique, aucune émission polluante
  • Adhérence forte: Formation par oxydation directe du magnésium, adhérence excellente
  • Performance exceptionnelle: Taux d'usure réduit de 16-25 fois, effet remarquable

Conclusions et discussion

Conclusions principales

  1. Préparation réussie: Formation réussie d'une couche de Mg(OH)₂ de 25 μm d'épaisseur en 4 heures en vapeur d'eau surchauffée à 200°C
  2. Amélioration significative des propriétés tribologiques: Le coefficient de frottement diminue de 0,4-0,5 à 0,12-0,17, le taux d'usure diminue de 16-25 fois
  3. Amélioration considérable de la résistance à la corrosion: Aucune corrosion évidente après 300 heures d'immersion dans une solution NaCl à 3,5%
  4. Changement du mécanisme d'usure: Transition d'une usure composite à un mécanisme doux de rectification-polissage

Points d'innovation technologique

  1. Innovation du procédé: Première utilisation de l'oxydation directe en vapeur d'eau surchauffée pour préparer une couche protectrice de Mg(OH)₂
  2. Caractéristiques écologiques: Procédé vert, sans pollution chimique
  3. Performance exceptionnelle: Amélioration simultanée de la résistance à l'usure et à la corrosion
  4. Mécanisme clair: L'oxydation directe assure une excellente liaison interfaciale

Limitations

  1. Température de traitement: Nécessite un traitement à haute température de 200°C pendant 4 heures
  2. Limitation d'épaisseur: L'épaisseur actuelle de la couche d'environ 25 μm peut être insuffisante pour les conditions extrêmes
  3. Plage de charges: Les charges d'essai sont relativement faibles (maximum 10N)
  4. Stabilité à long terme: Manque d'évaluation des performances en conditions de service prolongées

Directions futures

  1. Optimisation du procédé: Étude de l'influence des paramètres tels que la température et le temps sur l'épaisseur et les performances de la couche
  2. Amélioration des performances: Exploration de techniques de traitement composite pour améliorer davantage les performances
  3. Extension des applications: Vérification de l'effet du traitement dans les conditions d'ingénierie réelles
  4. Approfondissement du mécanisme: Étude approfondie du mécanisme tribologique de la couche de Mg(OH)₂

Évaluation approfondie

Points forts

  1. Forte innovativité de la méthode: La méthode d'oxydation en vapeur d'eau surchauffée est simple, novatrice et originale
  2. Conception expérimentale rationnelle: Caractérisation systématique et tests de performance, données fiables
  3. Résultats remarquables: Amélioration significative des performances de frottement et d'usure, valeur pratique élevée
  4. Importance environnementale: Le procédé vert répond aux exigences du développement durable
  5. Analyse du mécanisme appropriée: Révélation du mécanisme d'amélioration des performances par plusieurs méthodes

Insuffisances

  1. Plage de charges limitée: Charge maximale de seulement 10N, applicabilité aux charges lourdes à vérifier
  2. Absence de performance à long terme: Manque d'évaluation des performances et de la stabilité en service prolongé
  3. Analyse de coûts insuffisante: Absence d'analyse économique détaillée
  4. Scénarios d'application limités: Principalement pour les conditions de frottement sec, performances en environnement humide inconnues

Évaluation de l'impact

  1. Contribution académique: Fournit de nouvelles idées et méthodes pour le traitement de surface des alliages de magnésium
  2. Valeur pratique: Procédé simple, facile à industrialiser
  3. Importance environnementale: Conforme aux tendances du développement de la fabrication verte
  4. Promotion technologique: Susceptible d'être appliquée dans le domaine du traitement de surface des alliages de magnésium

Scénarios d'application applicables

  1. Couples de frottement à charge légère: Adapté aux composants de glissement à charge relativement faible
  2. Environnement corrosif: Composants d'alliage de magnésium dans les environnements corrosifs marins et chimiques
  3. Aérospatiale: Composants de frottement sensibles au poids
  4. Industrie automobile: Composants d'allègement des moteurs et systèmes de transmission

Références bibliographiques

L'article cite 22 références pertinentes, couvrant les principales voies technologiques du traitement de surface des alliages de magnésium, incluant l'anodisation, l'oxydation par décharge plasma électrolytique, la déposition physique en phase vapeur, la déposition chimique en phase vapeur et autres méthodes, fournissant un contexte technique suffisant et une base de comparaison pour cette recherche.


Évaluation générale: Cet article est une recherche de qualité relativement élevée en science des matériaux, proposant une nouvelle méthode simple et écologique de traitement de surface des alliages de magnésium, avec une conception expérimentale rationnelle et des résultats convaincants. Cette méthode présente des effets remarquables dans l'amélioration des propriétés tribologiques des alliages de magnésium et possède de bonnes perspectives d'application. Il est recommandé de poursuivre les études d'évaluation des performances à long terme et de vérification des applications d'ingénierie.