Wear and corrosion properties of Mg(OH)$_2$ compound layer formed on magnesium alloy in superheated water vapor

Peng, Wang
The wear resistance of magnesium and its alloys is very poor due to their inherent low hardness and poor tribological properties. Improving the wear resistance of magnesium and its alloys plays a significant role in expanding their application range. Various surface treatments have been used to produce protective coatings or layers for solving this problem. In this work, the Mg(OH)$_2$ layer with a thickness about 25 microns was directly formed on AZ91 magnesium alloy by oxidizing in superheated water vapor. SEM and XRD were employed to characterize the microstructure and phase composition of oxidized layer. The effect of oxidized layer on the friction and wear properties of magnesium alloy against the bearing steel ball were evaluated by using a reciprocating friction and wear test apparatus. The results showed that layer exhibited low friction coefficients and extremely small wear loss compared to the untreated substrate. Keywords: Magnesium alloy; Mg(OH)$_2$ layer; superheated water vapor; wear resistance.
academic

Proprietà di usura e corrosione dello strato composito Mg(OH)2_2 formato su lega di magnesio in vapore acqueo surriscaldato

Informazioni Fondamentali

  • ID Articolo: 2412.20959
  • Titolo: Wear and corrosion properties of Mg(OH)2_2 compound layer formed on magnesium alloy in superheated water vapor
  • Autori: Tianxiang Peng, Liang Wang (Dalian Maritime University)
  • Classificazione: cond-mat.mtrl-sci (Scienza dei Materiali)
  • Autore Corrispondente: Liang Wang (wlimt@dlmu.edu.cn)
  • Link Articolo: https://arxiv.org/abs/2412.20959

Riassunto

Il magnesio e le sue leghe presentano scarsa resistenza all'usura a causa della loro intrinseca bassa durezza e scarse proprietà tribologiche. Il miglioramento della resistenza all'usura delle leghe di magnesio è di fondamentale importanza per ampliare il loro campo di applicazione. In questo studio, uno strato di Mg(OH)2_2 dello spessore di circa 25 micrometri è stato formato direttamente sulla superficie della lega di magnesio AZ91 mediante ossidazione in vapore acqueo surriscaldato. La microstruttura e la composizione di fase dello strato ossidato sono state caratterizzate mediante SEM e XRD. L'effetto dello strato sulle proprietà di attrito e usura tra la lega di magnesio e una sfera di acciaio per cuscinetti è stato valutato utilizzando un dispositivo di prova di attrito e usura reciproco. I risultati hanno dimostrato che, rispetto al materiale base non trattato, questo strato presenta un coefficiente di attrito inferiore e una perdita di usura minima.

Contesto e Motivazione della Ricerca

Descrizione del Problema

  1. Problema Centrale: La bassa durezza intrinseca e le scarse proprietà tribologiche delle leghe di magnesio determinano una resistenza all'usura estremamente scarsa, limitando le loro applicazioni in componenti soggetti a usura per scorrimento
  2. Esigenze Applicative: Le leghe di magnesio, come uno dei materiali strutturali più leggeri, possiedono un eccellente rapporto resistenza-peso e hanno un valore significativo nell'industria aerospaziale e automobilistica
  3. Problemi di Corrosione: Le leghe di magnesio presentano scarsa resistenza alla corrosione in ambienti corrosivi e persino in condizioni umide

Importanza della Ricerca

  • Le caratteristiche di leggerezza delle leghe di magnesio conferiscono vantaggi critici in settori con rigorosi requisiti di efficienza del carburante e prestazioni
  • Il miglioramento della resistenza all'usura e alla corrosione rappresenta un collo di bottiglia tecnologico critico per ampliare il campo di applicazione delle leghe di magnesio
  • La tecnologia di trattamento superficiale è un approccio efficace per risolvere questo problema

Limitazioni dei Metodi Esistenti

I metodi di trattamento superficiale esistenti includono anodizzazione, conversione chimica, ossidazione per scarica al plasma, placcatura, trattamento per attrito-stirring, rivestimento, deposizione fisica da fase vapore, ecc., ma questi metodi generalmente:

  • Presentano processi complessi e costi elevati
  • Richiedono apparecchiature speciali e reagenti chimici
  • Possono generare inquinamento ambientale
  • Il legame tra rivestimento e substrato potrebbe essere insufficiente

Motivazione della Ricerca

Questo articolo propone un metodo di ossidazione in vapore acqueo surriscaldato semplice e rispettoso dell'ambiente, che richiede solo energia elettrica e una piccola quantità di acqua, senza altri materiali di consumo ed emissioni, formando uno strato protettivo di Mg(OH)2_2 attraverso l'ossidazione diretta del magnesio.

Contributi Principali

  1. Propone un nuovo metodo di trattamento superficiale ecologico e semplice: Sviluppa la tecnologia di ossidazione in vapore acqueo surriscaldato, che forma uno strato di Mg(OH)2_2 di spessore 25 μm dopo un trattamento di 4 ore a 200°C
  2. Migliora significativamente le proprietà tribologiche: Il coefficiente di attrito si riduce da 0,4-0,5 a 0,12-0,17, il tasso di usura diminuisce di 16-25 volte
  3. Aumenta notevolmente la resistenza alla corrosione: Dopo 300 ore di immersione in soluzione NaCl al 3,5%, la superficie rimane praticamente invariata
  4. Fornisce una valutazione sistematica delle prestazioni: Valuta completamente l'effetto del trattamento attraverso prove di attrito e usura in diverse condizioni di carico e prove di corrosione a lungo termine
  5. Rivela i cambiamenti nel meccanismo di usura: Transizione da usura composita (ossidazione-aratura-deformazione plastica-adesione) a meccanismo di rettifica-lucidatura

Spiegazione Dettagliata dei Metodi

Materiali e Preparazione dei Campioni

  • Materiale: Lega di magnesio AZ91D, composizione chimica (% in peso): Al(8,3-9,7), Zn(0,35-1,0), Mn(0,15-0,5), Mg(resto)
  • Campioni: Ricavati da barre di diametro 12 mm, spessore 5 mm
  • Pretrattamento: Levigatura meccanica con carta vetrata a carburo di silicio da 400-1200 grana

Processo di Trattamento Ossidativo

  1. Apparecchiatura: Contenitore in acciaio inossidabile, volume totale 4,4 litri
  2. Parametri di Processo:
    • Temperatura: 200°C
    • Tempo di mantenimento: 4 ore
    • Mezzo: Vapore acqueo surriscaldato
  3. Meccanismo di Reazione: Mg + 2H₂O → Mg(OH)₂ + H₂
  4. Caratteristiche:
    • Nessun pretrattamento aggiuntivo richiesto
    • Consuma solo energia elettrica e una piccola quantità di acqua
    • Nessun altro materiale di consumo ed emissioni

Metodi di Caratterizzazione

  1. Analisi XRD: Rigaku D/Max-Ultima, radiazione Cu Kα (λ=1,54 Å), 40kV/40mA
  2. Osservazione SEM: Microscopio elettronico a scansione SUPRA 55, equipaggiato con sistema di analisi EDX
  3. Misurazione dello Spessore: Attraverso osservazione microscopica della sezione trasversale levigata

Test delle Prestazioni

  1. Prova di Attrito e Usura:
    • Apparecchiatura: Macchina di prova di attrito e usura HRS-2M (configurazione perno-disco)
    • Materiale controparte: Sfera di acciaio per cuscinetti GCr15 (diametro 5 mm)
    • Carico: 3N, 5N, 8N
    • Lunghezza di corsa reciproca: 5 mm, frequenza: 5 Hz, durata: 30 minuti
    • Ambiente: Temperatura ambiente, umidità relativa 40%, condizioni di scorrimento secco
  2. Prova di Corrosione: Prova di immersione in soluzione NaCl al 3,5%, osservazione della morfologia di corrosione a diversi tempi

Configurazione Sperimentale

Materiali di Prova

  • Materiale Base: Lega di magnesio AZ91D
  • Campioni di Confronto: Campione non trattato vs. campione trattato con ossidazione
  • Materiale Controparte: Sfera di acciaio per cuscinetti GCr15

Indici di Valutazione

  1. Indici Tribologici:
    • Coefficiente di attrito (monitoraggio continuo)
    • Tasso di usura (mm³N⁻¹m⁻¹)
    • Larghezza e profondità della traccia di usura
  2. Prestazioni di Corrosione: Cambiamenti nella morfologia superficiale durante la prova di immersione
  3. Microstruttura: Composizione di fase, morfologia superficiale, struttura della sezione trasversale

Condizioni di Prova

  • Intervallo di Carico: 3N, 5N, 10N
  • Durata della Prova: 30 minuti
  • Condizioni Ambientali: Temperatura ambiente, scorrimento secco
  • Mezzo Corrosivo: Soluzione NaCl al 3,5% in peso

Risultati Sperimentali

Caratterizzazione della Microstruttura

  1. Cambiamenti di Aspetto: La superficie dopo il trattamento presenta un colore nero uniforme e profondo
  2. Composizione di Fase: XRD conferma la formazione della fase Mg(OH)₂, con picchi caratteristici a 32,8°, 38,1°, 58,7°, 62,2° e 68,9°
  3. Spessore dello Strato: Circa 25 μm, denso e uniforme senza difetti evidenti
  4. Composizione Elementare: EDX mostra un rapporto atomico O/Mg prossimo a 2:1, confermando Mg(OH)₂

Prestazioni di Attrito e Usura

Risultati del Campione Non Trattato

  • Coefficiente di Attrito: 0,35-0,45 (carichi 3N, 5N), 0,3-0,55 (carico 10N)
  • Larghezza della Traccia: 930-1000 μm (3N), 1320-1400 μm (5N), 1520-1600 μm (10N)
  • Profondità della Traccia: 45 μm (3N), 102 μm (5N), 127 μm (10N)
  • Tasso di Usura: 63,95×10⁻⁷ (3N), 84,14×10⁻⁷ (5N), 79,66×10⁻⁷ mm³N⁻¹m⁻¹ (10N)

Risultati del Campione Trattato con Ossidazione

  • Coefficiente di Attrito: 0,12-0,17 (tutte le condizioni di carico)
  • Larghezza della Traccia: 535 μm (3N), 562 μm (5N), 622 μm (10N)
  • Profondità della Traccia: 5 μm (3N), 7 μm (5N), 12 μm (10N)
  • Tasso di Usura: 3,96×10⁻⁷ (3N), 3,62×10⁻⁷ (5N), 3,12×10⁻⁷ mm³N⁻¹m⁻¹ (10N)

Entità del Miglioramento delle Prestazioni

  • Riduzione del Coefficiente di Attrito: Circa 70-75%
  • Riduzione del Tasso di Usura: 16 volte (3N), 23 volte (5N), 25 volte (10N)
  • Superficie della Traccia: Liscia e uniforme, senza graffi evidenti, aspetto lucidato

Prestazioni di Corrosione

  • Campione Non Trattato: Corrosione localizzata dopo 12 ore, prodotti di corrosione diffusi dopo 48 ore, corrosione grave dopo 72 ore, corrosione parziale completa dopo 300 ore
  • Campione Trattato con Ossidazione: Dopo 300 ore di immersione, la superficie rimane praticamente invariata, nessun prodotto di corrosione

Analisi del Meccanismo di Usura

  1. Campione Non Trattato:
    • Basso carico: Usura ossidativa e aratura
    • Alto carico: Meccanismo composito di aratura, deformazione plastica e adesione
  2. Campione Trattato con Ossidazione: Meccanismo di rettifica e lucidatura, senza graffi, adesione o deformazione plastica

Confronto con Lavori Correlati

Confronto delle Prestazioni con Altri Metodi di Trattamento Superficiale

  1. Rivestimento Ti-DLC: Coefficiente di attrito <0,12, tasso di usura ridotto di 2-3 ordini di grandezza
  2. Rivestimento Composito TiC/Co/Y₂O₃: Tasso di usura ridotto di circa 7 volte
  3. Rivestimento Autolubrificante Ti-MoS₂: Volume di usura ridotto del 43,88%-89,78%
  4. Rivestimento Gradiente Funzionale Ni-WC/Al-Ni: Resistenza all'usura migliorata di 5-8 volte
  5. Rivestimento Gradiente Nb₂O₅/Mg: Tasso di usura ridotto di più di un ordine di grandezza

Vantaggi di Questo Metodo

  • Processo Semplice: Nessuna apparecchiatura complessa e reagenti chimici richiesti
  • Rispetto Ambientale: Richiede solo acqua ed energia elettrica, nessuna emissione di inquinanti
  • Adesione Forte: Formato attraverso l'ossidazione diretta del magnesio, adesione eccellente
  • Prestazioni Eccellenti: Tasso di usura ridotto di 16-25 volte, effetto significativo

Conclusioni e Discussione

Conclusioni Principali

  1. Preparazione Riuscita: Preparazione riuscita di uno strato di Mg(OH)₂ di spessore 25 μm in vapore acqueo surriscaldato a 200°C per 4 ore
  2. Miglioramento Significativo delle Proprietà Tribologiche: Il coefficiente di attrito si riduce da 0,4-0,5 a 0,12-0,17, il tasso di usura diminuisce di 16-25 volte
  3. Aumento Sostanziale della Resistenza alla Corrosione: Nessuna corrosione evidente dopo 300 ore di immersione in soluzione NaCl al 3,5%
  4. Cambiamento del Meccanismo di Usura: Transizione da usura composita a meccanismo di rettifica e lucidatura dolce

Punti di Innovazione Tecnica

  1. Innovazione del Processo: Primo utilizzo dell'ossidazione diretta in vapore acqueo surriscaldato per preparare lo strato protettivo di Mg(OH)₂
  2. Caratteristiche Ecologiche: Processo verde, nessuna inquinamento chimico
  3. Prestazioni Eccellenti: Migliora simultaneamente la resistenza all'usura e alla corrosione
  4. Meccanismo Chiaro: L'ossidazione diretta garantisce un'adesione interfacciale eccellente

Limitazioni

  1. Temperatura di Trattamento: Richiede trattamento ad alta temperatura di 200°C per 4 ore
  2. Limitazione dello Spessore dello Strato: Lo spessore dello strato attuale è di circa 25 μm, potrebbe essere insufficiente per condizioni di lavoro estreme
  3. Intervallo di Carico: Il carico di prova è relativamente basso (massimo 10N)
  4. Stabilità a Lungo Termine: Mancanza di valutazione delle prestazioni in condizioni di servizio a lungo termine

Direzioni Future

  1. Ottimizzazione del Processo: Ricerca dell'effetto di parametri quali temperatura e tempo sullo spessore dello strato e sulle prestazioni
  2. Miglioramento delle Prestazioni: Esplorazione di tecniche di trattamento composito per migliorare ulteriormente le prestazioni
  3. Estensione dell'Applicazione: Verifica dell'effetto del trattamento in condizioni ingegneristiche reali
  4. Approfondimento del Meccanismo: Ricerca approfondita del meccanismo tribologico dello strato di Mg(OH)₂

Valutazione Approfondita

Punti di Forza

  1. Forte Innovatività del Metodo: Il metodo di ossidazione in vapore acqueo surriscaldato è semplice e innovativo, con forte originalità
  2. Progettazione Sperimentale Razionale: Caratterizzazione sistematica e test delle prestazioni, dati affidabili
  3. Risultati Significativi: Ampio miglioramento delle prestazioni di attrito e usura, alto valore pratico
  4. Significato Ambientale: Il processo verde è conforme ai requisiti dello sviluppo sostenibile
  5. Analisi del Meccanismo Adeguata: Rivela il meccanismo di miglioramento delle prestazioni attraverso molteplici metodi

Insufficienze

  1. Intervallo di Carico Limitato: Il carico massimo è solo 10N, l'applicabilità a carichi pesanti rimane da verificare
  2. Mancanza di Prestazioni a Lungo Termine: Mancanza di valutazione delle prestazioni di servizio a lungo termine e della stabilità
  3. Analisi dei Costi Insufficiente: Mancanza di analisi economica dettagliata
  4. Scenari di Applicazione Limitati: Principalmente per condizioni di scorrimento secco, le prestazioni in ambienti umidi rimangono sconosciute

Valutazione dell'Impatto

  1. Contributo Accademico: Fornisce nuove idee e metodi per il trattamento superficiale delle leghe di magnesio
  2. Valore Pratico: Il processo è semplice, facile da industrializzare
  3. Significato Ambientale: Conforme alle tendenze dello sviluppo della produzione verde
  4. Promozione Tecnologica: Potrebbe trovare applicazione nel campo del trattamento superficiale delle leghe di magnesio

Scenari di Applicazione Appropriati

  1. Coppie di Attrito a Carico Leggero: Adatto a componenti di scorrimento con carichi relativamente bassi
  2. Ambienti Corrosivi: Componenti in lega di magnesio in ambienti corrosivi come marino e chimico
  3. Aerospaziale: Componenti di attrito sensibili al peso
  4. Industria Automobilistica: Componenti leggeri in motori e sistemi di trasmissione

Riferimenti Bibliografici

L'articolo cita 22 articoli correlati, coprendo i principali percorsi tecnologici del trattamento superficiale delle leghe di magnesio, inclusi anodizzazione, ossidazione per scarica al plasma, deposizione fisica da fase vapore, deposizione chimica da fase vapore e altri metodi, fornendo un background tecnico sufficiente e una base di confronto per questa ricerca.


Valutazione Complessiva: Questo è un articolo di ricerca di qualità relativamente elevata nel campo della scienza dei materiali, che propone un nuovo metodo di trattamento superficiale semplice e rispettoso dell'ambiente per le leghe di magnesio, con una progettazione sperimentale razionale e risultati convincenti. Questo metodo è molto efficace nel migliorare le proprietà tribologiche delle leghe di magnesio e ha buone prospettive di applicazione. Si consiglia di condurre ulteriori ricerche sulla valutazione delle prestazioni a lungo termine e sulla verifica dell'applicazione ingegneristica.