Comparison of Electroluminescence and Photoluminescence Imaging of Mixed-Cation Mixed-Halide Perovskite Solar Cells at Low Temperatures

Yuce-Cakir, Chen, Ogunniranye et al.

Halide perovskites have emerged as promising candidates for high-performance solar cells. This study investigates the temperature-dependent optoelectronic properties of mixed-cation mixed-halide perovskite solar cells using electroluminescence (EL) and photoluminescence (PL) hyperspectral imaging, along with current-voltage analysis. Luminescence images, which were converted to EL and PL external radiative efficiency (ERE) maps, revealed significant changes in the optoelectronic behavior of these devices at low temperatures. Specifically, we found that a significant source of heterogeneity in the low-temperature EL ERE maps below 240 K is related to local charge injection and extraction bottlenecks, whereas PL ERE maps show suppressed non-radiative recombination and significant improvements in efficiency throughout the investigated temperature range. The spatial distribution of ERE and its variation with applied current were analyzed, offering insights into charge-carrier dynamics and defect behavior. Our results reveal that while the perovskite layer exhibits enhanced ERE at low temperatures, charge injection barriers at the interfaces of the perovskite solar cells significantly suppress EL and degrade the fill factor below 240 K. These findings reveal that a deeper understanding of the performance of perovskite solar cells under low-temperature conditions is an essential step toward their potential application in space power systems and advanced semiconductor devices.

academic

低温下の混合カチオン混合ハライドペロブスカイト太陽電池の電致発光と光致発光イメージングの比較

基本情報

論文ID: 2510.14213
タイトル: Comparison of Electroluminescence and Photoluminescence Imaging of Mixed-Cation Mixed-Halide Perovskite Solar Cells at Low Temperatures
著者: Hurriyet Yuce-Cakir, Haoran Chen, Isaac Ogunniranye, Susanna M. Thon, Yanfa Yan, Zhaoning Song, Behrang H. Hamadani
分類: cond-mat.mtrl-sci physics.app-ph physics.optics
発表機関: 米国国立標準技術研究所(NIST)、ジョンズ・ホプキンス大学、トレド大学
論文リンク: https://arxiv.org/abs/2510.14213

要旨

本研究は、電致発光(EL)および光致発光(PL)ハイパースペクトラルイメージング技術を電流-電圧分析と組み合わせて、低温下における混合カチオン混合ハライドペロブスカイト太陽電池の光電特性を系統的に調査した。240K以下では、EL外部放射効率(ERE)マッピングの不均一性は主に局所的な電荷注入および抽出のボトルネックに由来することが判明した。一方、PL EREマッピングは非放射再結合の抑制を示し、効率が著しく向上した。結果は、ペロブスカイト層が低温下で増強されたERE を示す一方で、界面における電荷注入障壁が240K以下のELを著しく抑制し、充填因子を低下させることを示唆している。